Skiver 3 mm 5 mm 13 mm PMI strukturell skumkjerner ark 32 kg/m³ Kina

Merke: Fucell® 

Materiale: PMI-skum

Farge: Naturhvit                

Density: 32/52/75/110kg/m³

Regular Size: 1250x2500mm

CNC service: Kutting/boring/forming

Application: Aerospace/medical parts/sport parts


produktbeskrivelse

    Polymethacrylimide foam (PMI) refers to the foam whose main molecular chain is C-C chain and the molecular side chain contains imide structure, which can be manufactured by various methods. The foam is currently the highest strength and stiffness heat-resistant foam (180 ~ 240 ℃), can meet the high temperature, high pressure curing and prepreg process requirements. It has good compatibility with various types of resins, suitable for use as core material in high-performance sandwich structures, can replace honeycomb structures, and is isotropic, easy to be machined into various complex cross-sectional shapes, and It does not contain any freon, and is an environmentally friendly material. Its fire resistance meets relevant standards such as FAR 25.853 and AITM, representing the latest development field of high-performance polymer structural foam.

6.1.2 6.1.2 3mm 5mm 13mm PMI Structural Foam Cores Sheet 32kg m3 China-详情-1

PMI danner kjerneegenskaper: 

Tetthet
(kg / m³)

Modell

Mekaniske egenskaper ved romtemperatur

Middels temperatur 130℃ ytelse

Trykkfasthet

Kompresjonsmodul

Strekkfasthet

Strekkmodul

Forlengelse ved pause

Ren styrke

Skjærmodul

Bøyestyrke

Bøyemodul

Deflection

Lukket cellehastighet

Trykkfasthet

Kompresjonsmodul

Hastighet for dimensjonsendring

MPA

MPA

MPA

MPA

%

MPA

MPA

MPA

MPA

mm

%

MPA

MPA

Lengde bredde høyde
(Ratio%)

Teststandard

GB / T 8813-2008

GB / T 9641-1988

GB / T 1455-2008

GB / T 8812.2-2007

GB / T 10799-2008

GB / T 8813-2008

GB / T 8811-2008

32

FF32

0.32

14

0.66

28

3.8

0.28

7.6

0.86

31

22

99

0.27

11

0.22

0.2

0.46

FU30

0.42

20

0.56

39

0.69

-

-

1

31

30

-

0.35

16

0.22

0.23

0.49

40

FC40

0.6

34

0.9

54

1.7

0.4

19

1.3

55

15

-

0.4

17

-

-

-

FU40

0.72

29

1.2

51

3.4

-

-

1.7

58

33

-

0.52

24

0.22

0.24

0.59

52

FC52

0.9

41

1.2

73

1.9

0.73

27

1.6

70

19

99

0.62

28

0.15

0.15

0.32

FM52

0.9

51

1.3

81

1.2

1

26

1.5

65

15

97

0.5

24

0.2

0.2

0.34

FF52

1

43

1.5

77

3.1

0.9

24

2.1

76

22

99

0.6

27

0.28

0.3

0.46

75

FC72

1.4

59

1.8

101

2.3

1.2

40

2

92

13

99

0.9

43

0.21

0.22

0.35

FF75

1.8

72

2.4

113

3.6

1.6

45

3.4

117

20

98

1.1

49

0.2

0.16

0.48

FU75

1.7

75

2.2

89

3.8

1.2

37

3.3

105

23

-

1.1

48

0.19

0.24

0.33

110

FF110

3.2

138

3.9

200

2.7

2

63

5.5

195

19

98

1.7

77

0.19

0.19

0.4

FU110

2.2

93

3.3

160

3.6

2.2

63

4.5

143

21

-

1.4

62

0.23

0.21

0.48

200

FF200

8.5

317

7.5

410

2.4

-

-

13

449

22

99

3.8

141

0.44

0.41

0.54

Påføring: 

-High strength foam core structures

-Reduce weight in molded parts

6.1.2 6.1.2 3mm 5mm 13mm PMI Structural Foam Cores Sheet 32kg m3 China-详情-2

KONTAKT

Hot kategorier

Legg igjen en beskjed
Nettprat

Hei, vær så snill å legge igjen navn og e-postadresse her før du chatter på nettet, slik at vi ikke savner meldingen din og kontakter deg jevnt.